Stoodite 6-O is the open arc wire version of Stoodite 6 cobalt alloy that produces a medium hardness cobalt-chromium deposit for high temperature applications with good abrasive wear and good impact resistance. Stoodite 6 is the most versatile and widely used cobalt alloy. Chromium carbides contained in the deposit provide excellent resistance to many forms of chemical and mechanical degradation, including galling and cavitation erosion. It bonds well with all weldable steels, including stainless.

BUY NOW


Features

  • Abrasion Resistance: Excellent
  • Impact Resistance: Good
  • Corrosion Resistance: Good
  • Hardness (2 layers): HRC 35 - 40
  • Hot Hardness: Excellent
  • Magnetic: No
  • Deposit Layers: 2 Maximum
  • Surface Cross Check: No*
  • Machinability: Use carbide tools
*With proper preheat and slow cooling.


Industries

  • Repair and Maintenance

Welding Process

  • GMAW (MIG/MAG)

Recommended Welding Parameters

Current 340-360 A
Conditional Statement Flat
TTW Dist. 3/4-1 in.
TTW Dist. 19-25 mm
Voltage 26-28 V
Wire Diameter 3/32 in.
Wire Diameter 2.4 mm

Classifications

Grade 2011 ERCCoCr-A
Name A5.21

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
C Co Cr Fe Mn Mo Ni Si W
1.2 % balance % 31.5 % 2.7 % 1.2 % 0.1 % 0.3 % 0.4 % 4.6 %

Chemical composition values are typical and were developed in accordance with AWS A5.21 procedures. Actual test results may vary depending on welding parameters, degree of dilution and base metal composition.

Minimum preheat recommended is 400°F (204°C). Required preheat will depend on base material composition and component dimensions.