Stoody HB-NoMag was designed to be a non-magnetic, crack free hardbanding alloy to be applied to non-magnetic down hole tooling and equipment. HB-NoMag produces a uniform distribution of small primary metal carbides in a fully austenitic chromium manganese matrix. Deposits are useful for rebuilding manganese, chrome-manganese and nitronic,non-magnetic stainless steel parts subject to severe impact loading combined with abrasion. HB-NoMag can be applied in multiple layers without spalling with proper welding procedures on austenitic manganese base metal.

BUY NOW


Features

  • Non-magnetic, crack free hardbanding of non-magnetic down hold tooling and equipment
  • Useful for rebuilding manganese, chrome-manganese and nitronic, non-magnetic stainless steel parts subject to severe impact loading combined with abrasion
  • Abrasion resistance three times superior to that of an austenitic manganese deposit as measured on the G65 test
  • Can be applied in multiple layers without spalling with proper welding procedures on austenitic manganese base metal


Typical Tensile Properties

Shielding Gas
75% Ar - 25% CO2

Deposition Data

Current 200-420 A
Deposition Type 3
Diameter 1/16 in.
Diameter 1.6 mm
Shielding Gas 75% Ar - 25% CO2
TTW Dist. 1/2-3/4 in.
TTW Dist. 13-19 mm
Voltage 22-32 V
Wire Feed Speed 230-365 in./min
Wire Feed Speed 584-927 cm/min

Typical Weld Metal Analysis %

C Cr Fe Mn Other
2.0 % 14.5 % BAL % 16.0 % 5.5 %