OK Autrod 310
A continous solid corrosion resisting chromium-nickel wire for welding of heat resistant austenitic steels of the 25% Cr, 20% Ni types. OK Autrod 310 has a good general oxidation resistance especially at high temperatures due to its high Cr content. The alloy is fully austenitic and therefore sensitive to hot cracking. Common applications are industrial furnaces and boiler parts as well as heat exchangers.
Typical Charpy V-Notch Properties
as welded | ||||
Typical Tensile Properties
Condition | Elongation | Tensile Strength | Yield Strength |
As Welded | 43 % | 590 MPa (86 ksi) | 390 MPa (57 ksi) |
Deposition Data
Current | Deposition Rate | Diameter | Voltage | Wire Feed Speed |
50-140 A | 0.8-2.7 kg/h (1.8-6.0 lb/h) | 0.8 mm (0.030 in.) | 16-22 V | 3.4-11.0 m/min (134-433 in./min) |
80-190 A | 1.1-3.1 kg/h (2.4-6.8 lb/h) | 1.0 mm (0.040 in.) | 16-24 V | 2.9-8.4 m/min (114-331 in./min) |
180-280 A | 2.6-4.5 kg/h (5.7-9.9 lb/h) | 1.2 mm (0.047 in.) | 20-28 V | 4.9-8.5 m/min (193-335 in./min) |
230-350 A | 3.0-5.2 kg/h (6.6-11. lb/h) | 1.6 mm (1/16 in.) | 24-28 V | 3.2-5.5 m/min (126-217 in./min) |
Classifications
Wire Electrode |
EN ISO 14343-A : G 25 20 SFA/AWS A5.9 : ER310 |
Approvals
Grade | EN 13479 |
Society | CE |
Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
Alloy Type | Fully austenitic (25 % Cr - 20 % Ni) |
Shielding Gas | M12, M13 (EN ISO 14175) |
Typical Weld Metal Analysis %
Typical Weld Metal Analysis % | ||||||||||||||
C | Cr | Mn | Ni | P | S | Si | ||||||||
0.10 % | 25 % | 1.7 % | 20 % | 0.010 % | 0.015 % | 0.4 % | ||||||||
Typical Wire Composition % | ||||||||||||||
0.10 % | 25.8 % | 1.6 % | 20.7 % | - | - | 0.4 % |