Stoody®C-S semi-automatic wire for submerged arc operation is a tubular nickel based wire developed for harsh environments of temperature and corrosion. The work hardening properties of this alloy make it especially resistance to metal-to-metal wear under conditions of high temperature and impact. It retains hardness up to 1200°F (650°C) and has a low coefficiency of friction. Deposits are dense and smooth.
- Dense smooth deposits.
- Especially resistant to metal-to-metal wear under high temperature and impact.
- Nickel-based wire for submerged arc process.
- Retains hardness up to 1200°F (650°C).
- Hardfacing overlays for: Continuous caster rolls, Piercing mill rolls (tips), Hot forging dies, Hot trimming punches, Rotary forge hammers, Tong bits, Guide rolls, Flow controls valves.
Typical Tensile Properties
|Current||Deposition Type||Diameter||TTW Dist.||Voltage|
|350-400 A||Subarc||3.2 mm (1/8 in.)|
|350-400 A||Full Range||3.2 mm (1/8 in.)||32-38 mm (1 1/4-1 1/2 in.)||28-30 V|
|250-300 A||Full Range||2.4 mm (3/32 in.)||25-32 mm (1-1 1/4 in.)||28-30 V|
|250-300 A||Subarc||2.4 mm (3/32 in.)|
Typical Weld Metal Analysis %
|0.1 %||16.0 %||5.0 %||BAL %||20.0 %|